1.High density
2.High Strength
3.Good toughness
4.High grinding efficiency
for the ceramics
for the glaze, paint, coating
for the zirconia silicate ,aluminum oxide ,quartz ,silicon carbide etc
for kaolin , titanium oxide ,mining’s etc
Items | Specification |
Al2O3 content | ≥92% |
SiO2 content | ≤7% |
Bulk Density | 3.65±0.05/cm3 |
Hardness(Mohs) | 9 |
Water absorption | ≤0.01% |
Self wearing loss (within 24hours) | ≤0.01% |
Anti-compression rate(Mpa) | ≥2000Mpa |
Color | White |
Size(mm) | Size(mm) | Size(mm) |
0.5 | 8.0 | 35 |
1.0 | 10.0 | 40 |
2.0 | 13.0 | 50 |
3.0 | 15.0 | 60 |
4.0 | 20.0 | 70 |
5.0 | 25.0 | 80 |
6.0 | 30.0 | --- |
M=3.14×R2×D×L×(25%-50%)÷1000
M: Total quantity of ceramic ball
D: Density (g/cm3)
R: Radius of the mill (cm)
L: Length of the mill (cm)
1.High density
2.High Strength
3.Good toughness
4.High grinding efficiency
for the ceramics
for the glaze, paint, coating
for the zirconia silicate ,aluminum oxide ,quartz ,silicon carbide etc
for kaolin , titanium oxide ,mining’s etc
Items | Specification |
Al2O3 content | ≥92% |
SiO2 content | ≤7% |
Bulk Density | 3.65±0.05/cm3 |
Hardness(Mohs) | 9 |
Water absorption | ≤0.01% |
Self wearing loss (within 24hours) | ≤0.01% |
Anti-compression rate(Mpa) | ≥2000Mpa |
Color | White |
Size(mm) | Size(mm) | Size(mm) |
0.5 | 8.0 | 35 |
1.0 | 10.0 | 40 |
2.0 | 13.0 | 50 |
3.0 | 15.0 | 60 |
4.0 | 20.0 | 70 |
5.0 | 25.0 | 80 |
6.0 | 30.0 | --- |
M=3.14×R2×D×L×(25%-50%)÷1000
M: Total quantity of ceramic ball
D: Density (g/cm3)
R: Radius of the mill (cm)
L: Length of the mill (cm)
湘ICP备12012704号 All Rights Reserved © 2010-2028 Zr-Product.com
Tel: 0086-731-84427228
Fax: 0086-731-84483877
Add: No.766 Wuyi Road, Changsha, China
湘ICP备12012704号 All Rights Reserved © 2010-2028 Zr-Product.com