1.High mechanical strength
2.Good wear resistance
3.Good heat resistance
4.Corrosion resistance
| Items | Specification |
| Density | 6.03 g/cc |
| Bending strength | 1000MPa |
| Fracture toughness | 5~8 Mpa.m 1/2 |
| Vickers hardness | 13 Gpa |
| pyroconductivity | 2 W/M K |
| linear expansion coefficient | 10.5 |
| dielectric coefficient | 11*106 V/m |
1. High grinding efficiency: the specific gravity is 1.6 times more than ordinary zirconia beads,it has higher grinding efficiency under the same conditions.
2. Good fluidity. With good roundness and smooth surface ,the abrasion of the equipment is lower than other grinding media.
3. Impact resistance and low wear: with good toughness,it will don’t crack and peel in the high-speed and high-concentration machine.The wear loss is only 1/2 of zirconia silicate bead.
4. Low cost: comprehensive cost reduction of medium wear ,power consumption ,lab ,equipment etc,
Paints, ink,pigment,dye
Magnetic materials,piezoelectric ceramics,Dielectric Ceramics
Medicine,food, cosmetics
Electric ceramics, refractory materials, structure ceramics
| Item | Specification |
| Composition wt% | 94.5% ZrO2 5.25% Y2O3 |
| Compression strength | ≥ 2250 |
| Hardness Moh’s | >9.0 |
| Bulk Density Kg/L | ≥3.60g/cm3 |
| Specific Density g/cm3 | ≥6.02g/cm3 |
| water absorption | ≤0.01% |
| Wear loss | ≤0.01% |
| Color | White |
7.5*7.5mm,10*10mm,12.7*12.7mm,15*15mm
1.High mechanical strength
2.Good wear resistance
3.Good heat resistance
4.Corrosion resistance
| Items | Specification |
| Density | 6.03 g/cc |
| Bending strength | 1000MPa |
| Fracture toughness | 5~8 Mpa.m 1/2 |
| Vickers hardness | 13 Gpa |
| pyroconductivity | 2 W/M K |
| linear expansion coefficient | 10.5 |
| dielectric coefficient | 11*106 V/m |
1. High grinding efficiency: the specific gravity is 1.6 times more than ordinary zirconia beads,it has higher grinding efficiency under the same conditions.
2. Good fluidity. With good roundness and smooth surface ,the abrasion of the equipment is lower than other grinding media.
3. Impact resistance and low wear: with good toughness,it will don’t crack and peel in the high-speed and high-concentration machine.The wear loss is only 1/2 of zirconia silicate bead.
4. Low cost: comprehensive cost reduction of medium wear ,power consumption ,lab ,equipment etc,
Paints, ink,pigment,dye
Magnetic materials,piezoelectric ceramics,Dielectric Ceramics
Medicine,food, cosmetics
Electric ceramics, refractory materials, structure ceramics
| Item | Specification |
| Composition wt% | 94.5% ZrO2 5.25% Y2O3 |
| Compression strength | ≥ 2250 |
| Hardness Moh’s | >9.0 |
| Bulk Density Kg/L | ≥3.60g/cm3 |
| Specific Density g/cm3 | ≥6.02g/cm3 |
| water absorption | ≤0.01% |
| Wear loss | ≤0.01% |
| Color | White |
7.5*7.5mm,10*10mm,12.7*12.7mm,15*15mm
湘ICP备12012704号 All Rights Reserved © 2010-2028 Zr-Product.com
Tel: 0086-731-84427228
Fax: 0086-731-84483877
Add: No.766 Wuyi Road, Changsha, China
湘ICP备12012704号 All Rights Reserved © 2010-2028 Zr-Product.com
Location :